Material: |
99% Alumina Ceramic |
Color: |
Light Yellow |
Density: |
3.9 G/cm³ |
Certifications: |
ROHS ISO9001 |
Hardness: |
10.7 Gpa |
Size: |
Customized |
Flexural Strength: |
300 Mpa |
Thermal Conductivity: |
25 W/(m.k) |
Insulation Breakdown Intensity: |
18 KT/mm |
OEM,ODM: |
Acceptable |
Material: |
99% Alumina Ceramic |
Color: |
Light Yellow |
Density: |
3.9 G/cm³ |
Certifications: |
ROHS ISO9001 |
Hardness: |
10.7 Gpa |
Size: |
Customized |
Flexural Strength: |
300 Mpa |
Thermal Conductivity: |
25 W/(m.k) |
Insulation Breakdown Intensity: |
18 KT/mm |
OEM,ODM: |
Acceptable |
Porous corrosion Resistance 99% Al2O3 Ceramic Abrasive Alumina Ceramic Tube
Alumina Ceramic
Alumina ceramic is a kind of material based on alumina (Al2O3), which is used in thick film integrated circuit. Alumina ceramics have good conductivity, mechanical strength and high temperature resistance. It needs to be noted that ultrasonic cleaning is needed.
Alumina ceramics are classified into high-purity type and ordinary type.
The high-purity alumina ceramics have a Al2O3 content of 99.9% or more. Since the sintering temperature is as high as 1650-1990 ° C and the transmission wavelength is 1 to 6 μm, the molten glass is generally used to replace the platinum crucible; Alkali-resistant metal corrosion is used as a sodium lamp; it can be used as an integrated circuit substrate and high-frequency insulation material in the electronics industry.
| Properties | Unit | Steatite ceramic | 95% Al2O3 | 99% Al2O3 | Zirconia Ceramic |
| Density | g/cm³ | 2.8 | 3.6 | 3.8 | 5.6 |
| Flexural strength | Mpa | 145 | 300 | 300 | 354 |
| Max Working Temperature | ℃ | 1100 | 1400 | 1600 | 1400 |
| Sintering temperature | ℃ | 1350 | 1700 | 1750 | 1550 |
| Heat resistance | T(℃) | 200 | 220 | 200 | 350 |
| Hardness | Gpa | 5.7 | 7 | 10.7 | 12.3 |
| Elastic modulus | Gpa | 120 | 275 | 320 | 205 |
| Poissons ratio | - | 0.21 | 0.22 | 0.22 | 0.30 |
| Linear expansion coefficient | x 10-6/℃ | 7.9 | 7.1 | 7.8 | 9 |
| Insulation breakdown Intensity | KT/mm | 10 | 16 | 18 | 15 |
| Thermal conductivity | w/(m.k) | 2.5 | 20 | 25 | 2.5 |
| Specific Heat | *10-3J/(kg*K) | 0.75 | 0.78 | 0.78 | 0.4 |